A Preliminary Report on FortiPhy™ XVD Performance





Oct 21, 2022


John B. Woodford, Ph.D and Mohumad al-Zoubi, Ph.D., Argonne National Laboratory

A preliminary report from Argonne Laboaratory shows Phygen’s FortiPhy™ XVD technology provides considerable protection to sliding surfaces while reducing friction and wear in lubricated contacts.


To protect a vulnerable surface from wear or chemical attack, or to enhance its friction behavior, it is frequently advisable to coat the surface with a hard film. Treating a part made from a weak material is generally more economical than constructing an entire part out of a more durable material. However, care must be taken in selecting the coating and matching it to the substrate, particularly in tribological applications: hard coatings can become a source of highly abrasive wear particles.

Among the hard coatings in current use are metal nitrides, especially titanium, chromium, and zirconium; polycrystalline and nanocrystalline diamond; cubic boron nitride; and tetrahedral amorphous carbon. These may be deposited in several different ways, although two are primarily used: physical vapor deposition (PVD) and chemical vapor deposition (CVD).

Previously, PVD chromium nitride (CrN) hard coatings have commonly suffered from poor homogeneity due to the presence of high volume fractions of entrained Cr droplets, and this has impaired their overall hardness, friction coefficient, and wear resistance. However, the FortiPhy™ XVD surface armor we examined in this study were apparently almost all single-phase nitride, with only a small fraction of entrained Cr, an apparently noncolumnar grain structure, and resultant high toughness and wear resistance. Here at Argonne, we have conducted preliminary tests on Phygen’s thin-film coatings.

Sample Description

We sent three hardened H-13 tool steel flats, a dozen M50 stainless steel balls, and two pieces of single-crystal Si wafer to Phygen for coating. Each flat and four of the balls were coated with a slightly different CrN formulation/process. The two wafers were coated with Phygen’s “best” CrN.

The flats and balls were intended for use in friction and wear tests, and the Si wafers were for characterization of the film. One of the wafers was scribed on its back with a diamond stylus and cracked, and the cross section was examined by scanning electron microscopy (SEM).

Phygen’s CrN: Physical Features

All pictures in this section were taken with a JEOL 840A scanning electron microscope (SEM). Figure 1a shows a high-magnification secondary electron (SE) plan view of the coated wafer, while Figure 1b shows a backscattered electron image (BEI) of the same area. The bright spheres are entrained Cr droplets. Note that the total percentage of area covered by these droplets is quite small, and that the largest droplet is only ca. 1 micrometer across. Figure 2a shows an SE cross-section of the film, and Figure 2b is a BEI of the same area.

It is not clear how much of the brightness variation in the BE image is due to entrained Cr (Zcontrast) and how much arises from topography. However, three distinct zones may be observed in the layer. Closest to the Si substrate (i.e., the right side of the image) is an area ca. 100 nm thick, bright in BE and showing signs of a very fine, possibly columnar grain structure in SE.

The central zone, some 500-600 nm thick, appears mostly dark in BE and has a texture in SE suggestive of flat grains parallel to the film surface. Finally, the uppermost zone is quite bright in BE, and in SE exhibits a texture suggesting a more equiaxed grain structure.

The low abundance of entrained droplets suggests that this film may not exhibit the poor wear properties of conventionally grown coatings. In addition, no porosity is evident in the film, indicating that it should be tougher than highly porous coatings. This increase in fracture toughness arises from the tendency of voids to act as crack nucleation sites; lacking such sites, the film should be more resistant to fracture

Figure 1a

Scanning Electron Microscope (SE) image, plan view of CrN film.

Figure 1b

BSE image, plan view of CrN film, same location as Figure 1a.

Figure 2a

SE image, cross-section of CrN film on Si. the Si substrate is to the right of the film.

Figure 2b

BE image, cross-section of CrN film on Si, same location as Figure 2a.

FortiPhy™ XVD: Friction/Wear Properties

The three CrN-coated flats and one uncoated H-13 steel flat were subjected to an endurance wear test in the presence of Fischer-Tropsch (FT) synthetic diesel fuel. The tests were conducted in a Cameron-Plint high-frequency reciprocating rig (HFRR), which moved the flats back and forth under a fixed 0.25 in. 52100 steel ball carrying a load of 10 N. Under this load and ball size, the peak and average Hertzian contact stresses were 900 and 600 MPa, respectively. Wear track length was 21 mm, test duration was 24 hr., and reciprocation frequency was 3 Hz. Total sliding distance for the test was thus ca. 10.9 km.

Figure 3 shows the friction coefficient traces for the three different coatings and the uncoated steel. All three coatings offer a reduction in friction over uncoated steel in FT fuel.

CrN #1 shows the least improvement, but is still ca. 20% lower than steel/steel. CrN #2 exhibits the lowest average friction coefficient (ca. 0.09), but also has a great deal of variation in friction (±0.02), a feature shared by CrN #1. CrN #3 has the best consistency in friction coefficient and has only slightly higher friction coefficient on average than CrN #2.

Examination of the wear tracks on the three coated flats showed no sign of wear. There was an apparent transfer layer of steel from the counterface, but nothing more. The uncoated flat had a distinct wear track, but optical profilometry showed it to be partially filled with material transferred from the ball. Because of this, it was impossible to measure wear rates on the flats.

The wear scars on the M50 balls were considerably easier to measure. Figure 4 is a bar graph of the volume of material lost from the balls; this is a critical design parameter for considering the degree of counterfacial wear in applications where a coated part slides against an uncoated surface. Here, CrN #1 is inferior to not only the other two coatings but to steel/steel.

CrN #2 is comparable to steel/steel, and CrN #3 is superior. However, the differences between the four results are sufficiently small that they could be attributed to measurement error; lacking a larger number of wear tests for statistical analysis, we could draw no firm conclusions from the wear data.

Based on these results, it appears that CrN #3 is the best overall in FT-fuel-lubricated applications–it wears the counterface about as much as uncoated steel while providing a substantial reduction in friction over that of uncoated steel in FT fuel. The low spread in friction value compared to that of CrN #1 and #2 may indicate a more homogeneous coating.

Patented-FortiPhy high performance surface coating improves toughness and reduces friction on dies, molds and tooling used in metal forming, die casting and injection molding applications.
Figure 5: SE image of indent in CrN #1 on H-13 steel.
FortiPhy high performance surface and tool coatings, using a patented plasma acceleration process, significantly increase durability and toughness while reducing friction, wear and corrosion in injection molding, die casting and metal forming applications
Figure 6: SE image of indent in CrN #2 on H-13 steel.

Phygen provides FortiPhy higher performance metal surface coatings for metal forming, die casting and injection molding applications. These PVD CrN tool coatings supply increased uptime and abrasive wear resistance.
Figure 7: SE image of indent in CrN #3 on H-13 steel.

Figure 3

Plot of friction coefficient vs. sliding distance for reciprocating tests described in the text.

Figure 4

Graph comparing ball wear rates for the reciprocating tests described in the text.

FortiPhy™ XVD: Other Mechanical Properties

The adhesion of the coating and its fracture toughness were qualitatively determined by indentation. Each of the three H-13 flats was indented with a Rockwell hardness tester in Rockwell A mode (60 kg load, diamond brale indenter). The indentations were examined by SEM. Figures 5-7 show the indentations on CrN #1, #2, and #3, respectively.

Although some delamination is observed in #1 and #3, the coating adhered extremely well to the area around the indentations. Under the same conditions, a diamond-like carbon (DLC) coating with a high percentage of sp3-bonded carbon delaminated in a large area around the indentation. The cracks radiating outward from the indentation are not very long (ca. 10-30 micrometers), a further indication of the film toughness.

FortiPhy™ XVD as an NFC Undercoat

One potential use for this coating is as an undercoat for Argonne’s near-frictionless carbon (NFC), a form of DLC deposited by plasma-assisted chemical vapor deposition (PACVD). In dry inert environments, NFC coatings exhibit the lowest friction coefficient of any solid material, i.e., 0.001. Even in lubricated or open-air conditions, NFC-coated parts show extremely low wear and friction. Phygen’s CrN may be used to support NFC films and to provide enhanced part protection if the NFC coating wears through or otherwise fails.

It is impossible to coat NFC onto most materials without first applying a bond coat by sputtering or PACVD; because chromium has been used successfully as a bond coat, it was hoped that NFC could be deposited directly onto CrN. This was attempted with one of the pieces of CrN-coated silicon wafer. The attempt was unsuccessful. Although a carbonaceous layer was deposited onto the CrN, it was completely graphitic and peeled off readily. We intend to try using our current bond coating technology as an intermediate layer, but that has not been done yet.


Phygen’s FortiPhy™ XVD technology affords considerable protection to sliding surfaces, and it reduces friction and wear in lubricated contacts. Its homogeneity is quite good, which should translate into improved mechanical properties.

Figure 5

SE image of indent in CrN #1 on H-13 steel.

Figure 6

 SE image of indent in CrN #2 on H-13 steel

Figure 7

SE image of indent in CrN #3 on H-13 steel.